Typical Cast Mechanical Properties
|Test||Unit of Measure||Nominal||Test Method|
|Tensile Strength||psi/MPa||13,8000/95||ASTM D 638|
|Tensile Modulus||psi/GPa||540,000/3.7||ASTM D 638|
|Tensile Elongation||%||4.6||ASTM D 638|
|Flexural Strength||psi/Mpa||22,000/151||ASTM D 790|
|Flexural Modulus||psi/Mpa||570,000/3.9||ASTM D 790|
|Heat Distortion Temp||°F/°C@264 psi||248/120||ASTM D638|
|Barcol Hardness||>40||ASTM D 2583|
A. Keep full strength catalyst levels between 1.0% – 3.0% of the total resin weight.
B. The resin is stable for three months from the date of production when stored in cool place and away from sunlight at no more than 25°F/77°F. During the hot summer months, no more than two months stability at 30°C/86°F should be anticipated. After extended storage, some drift may occur in gel time and viscosity.